RADIATION DEGRADATION OF CHITOSAN IN THE PRESENCE OF H2O2

In order to obtain the chitosan oligomers, chitosan was irradiated in the solid state with and without H2O2 as a radiation degradation sensitizer, respectively. At room temperature, the viscosity average-molecular weight (Mη) of chitosan was decreased from 1.6 × 106 to 2.2 × 105 at an absorbed dose of 72 kGy without H2O2, and decreased to 2.7 × 104 at 2 kGy in the presence of an appropriate H2O2 content. In addition, the radiation degradation rate of chitosan containing 38.2wt%H2O2 is 59 times higher than that in the solid state without H2O2. FT-IR analysis suggests that there is no obvious change in the chemical structure of irradiated chitosan with and without H2O2 at a dose below 20 kGy, compared with unirradiated chitosan. On the other hand, the degree of deacetylation (DD) of irradiated chitosan in the studied dose range changed slightly, while DD of irradiated chitosan with H2O2 increased significantly. The XRD pattern indicates that the irradiated chitosan with H2O2 has more perfect crystalline structure than unirradiated chitosan. Therefore, it could be expected that irradiation of chitosan using H2O2 as a sensitizer would be a very effective method to prepare low molecular weight chitosan,because of its feasibility and benignancy to environment.

作 者： Yi-hong Lu Gen-shuan Wei JING Peng   作者單位： Institute of Applied Chemistry, College of Chemistry, Peking University, Beijing 100871, China  刊 名： 高分子科學(xué)(英文版)  ISTIC SCI 英文刊名： CHINESE JOURNAL OF POLYMER SCIENCE  年，卷(期)： 2004 22(5)  分類號(hào)：   關(guān)鍵詞： Chitosan   Radiation degradation   H2O2   Structure  

【RADIATION DEGRADATION OF CHITOSAN IN】相關(guān)文章：

Flocculation Kinetics of Chitosan04-27

Cometabolic microbial degradation of trichloroethylene in the presence of toluene04-26

Degradation of 4-CP in an internal electrolysis system04-26

Degradation of 4-CP in an internal electrolysis system04-26

Isolation and Characterization of Microorganisms for Degradation of Minimal Oils and Fats at Low Temperatures04-27

Rapid degradation of bensulfuron-methyl upon repeated application in paddy soils04-26

Photocatalytic degradation of dye effluent by titanium dioxide pillar pellets in aqueous solution04-26

Degradation of phenol in an upflow anaerobic sludge blanket(UASB) reactor at ambient temperatureKE04-26

Degradation of phenol in an upflow anaerobic sludge blanket(UASB) reactor at ambient temperatureKE04-26

Aircraft Engine Sensor Fault Diagnostics Based on Estimation of Engines Health Degradation04-26